TECHNOLOGICAL TESTS FOR CERAMIC, REFRACTORY AND POWDER METALLURGY

 

Analysis/Test Code

Analysis/Test Name

Method/Explanation

Service Period (Workday)

Sample Amount

Service Fee

(VAT Included)

35-30-TS-01

Particle  Size Analysis

(by Laser Diffraction Method) Wet

Performed according to TS ISO 13320 Standard. (Laser Light Diffraction Method)

Sample should be sent in homogeneous form and the information on physical characteristics of the sample such as sample type, flocculation, viscousness, dissolvability etc. should be stated in the Analysis/Test Application Form.

3 days

500 g and particle size of the sample should be maximum 2 mm.

160,00 TL /Sample

35-30-TS-02

Particle Size Analysis

(by Laser Diffraction Method) Dry

Performed according to TS ISO 13320 Standard. (Laser Light Diffraction Method)

Sample should be sent in homogeneous form and the information on physical characteristics of the sample such as sample type, flocculation, viscousness, dissolvability etc. should be stated in the Analysis/Test Application Form.

3 days

1 kg and particle size of the sample should be maximum 2 mm.

210,00 TL /Sample

35-30-TS-15

Moulding  and  Drying Processes

-

5 days

5 kg

70,00 TL /Sample

35-30-TS-16

Plasticity Water In Mud

Performed according to TS 5396 Standard.

5 days

5-10 kg

50,00 TL /Sample

35-30-TS-17

Plastic Water (Plastic Limit)

Performed with Pfefferkorn method.

5 days

5-10 kg

50,00 TL /Sample

35-30-TS-18

Plasticity Water (Liquid Limit)

Performed with Atterberg method.

5 days

5-10 kg

50,00 TL /Sample

35-30-TS-19

Plasticity Index

(Plastic Limit-Liquid Limit)

 

Plastic Limit is determined with Pfefferkorn Method and Liquid Limit is determined with Atterberg Method.

5 days

5-10 kg

110,00 TL /Sample

35-30-TS-104

BET Spesific Surface Area

Information such as Brunauer, Emmett and Teller (BET) Method, Degas duration and temperature should be given in the Analysis/Test Application Form.

3 days

100 g or fragmentary sample

355,00 TL /Sample

35-30-TS-105

Multi Point BET  and  Pore Volume / Pore Size Distribution

Information such as Brunauer, Emmett and Teller (BET) Method, Degas duration and temperature should be given in the Analysis/Test Application Form.

3 days

100 g or fragmentary sample

705,00 TL /Sample

35-30-TS-106

Firing Test

Maximum firing temperature is 1650 °C.

5 days

0,5-1 kg

325,00 TL /Temperature Point